2014 aluminum is one of the strongest Heat-treatable alloys for screw machine applications. 2014 has good mechanical properties and has good weldability, but it has only fair corrosion resistance. It can be substituted for 2024 in many applications.
Applications: Screw Machine, Aerospace, General applications.
Aging: Artificial aging is most commonly used for this alloy. Tempering is widely used for most applications, T-4/T451, T-6/T651 are most commonly used.
| Chemistry Analysis | ||||||
|---|---|---|---|---|---|---|
| Titanium | Max | 0.15% | Manganese | 0.40 – | 1.20% | |
| Titanium/Zinc | Max | 0.2% | Copper | 3.9 – | 5.0% | |
| Silicon | 0.50 – | 1.20% | Chromium | Max | 0.10% | |
| Zinc | Max | 0.25% | Iron | Max | 0.70% | |
| Magnesium | 0.20 – | 0.80% | Aluminum | Balance |
| Temper Temperature | Yield 0.2% | Yield 0.2% | Ultimate Tensile Strength | % Elongation in 2” (50.8mm) | |
|---|---|---|---|---|---|
| 0.2% offset | 0.2% offset | ||||
| ksi | mpa | ksi | mpa | ||
| 0 Temper | 14 | 97 | 27 | 186 | 18 |
| T-4 | 42 | 290 | 62 | 427 | 20 |
| T-6 | 60 | 414 | 70 | 483 | 13 |
Machinability: 2014 machines easily in any condition
Specifications: AMS 4121, ASTM B211
Shapes Manufactured:
Flat Bars, Square Bars, Round Bars, Rings, Hollows, Discs, Blocks and special Shapes. Send us a drawing to see how we can save you material and Machining time!